TOTAL Polyethylene Lumicene® M 5510 EP
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E6QcLy_TOTAL-Polyethylene-Lumicene-M-5510-EP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumicene® mPE M5510 EP is a second generation metallocene high density homopolymer Polyethylene. Lumicene® mPE M5510 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The outstanding stiffness combined with good optical properties brings a significant down-gauging potential. The high density of Lumicene® mPE M5510 EP enables its use in applications with moisture barrier requirements, such as dry food packaging, and brings improved heat resistance, compared to commonly used HDPE. Lumicene® mPE M5510 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as bags, heavy-duty sacks, automatic packaging specialty film, mailing film and lamination. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.955 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 27.5 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 28.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 57.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 45.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 870 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 910 | % | ISO 527-3 |
| Dart Drop Test - Blown Film (40.0 µm) | 100 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 40.0 µm | 11.0 | kN/m | ISO 6383-2 |
| TD : 40.0 µm | 90.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 133 | °C | ISO 306 |
| Melting Temperature | 134 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 40 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 24 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 230 | °C |
| Extrusion instructions |
|---|
| BUR: 1.5:1 to 4.5:1Die Gap: 0.8 to 2.8 mm |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP733 | Southern Polymer, Inc. | HDPE | PRIMALENE |
| RapidVac™ VA-1510 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| THERMOLAST® K TF5PEN (Series: FC/AD/PE) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Niche PCABSN10BK | Niche Polymer, LLC | PC+ABS | Niche |
| Karina IVORY PVC COMPOUND -E 70900-35/ 1-E-AC (AS80NF)/K | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |