4LEX® 10F13500
| Category: | PC , Polycarbonate |
| Manufacturer: | 4Plas |
| Trademark: | 4LEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E4Oi43_4LEX-10F13500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4LEX 10F13500 is a MFI 14 to 16 Halogen Free FR-V0 Polycarbonate |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.50 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 60.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 40 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 15 | kJ/m² | ISO 180/1A |
| 23°C | 30 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 153 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Screw Speed | < 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9266-85 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Tislamid® PA66 PA66 15 GFR | Tisan | Nylon 66 | Tislamid® PA66 |
| ExxonMobil™ PP1064L1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Sylvin 8225-48FR Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9600-72 Green 3168 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |