MDF463 is a 15% glass fibre reinforced grade of nylon 6 that contains an impact modification system which offers superior low temperature performance - along with a stabilisation package to enhance component life in severe environmental conditions. This grade offers a good balance of rigidity and toughness over a wide temperature range.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 15% filler by weight
Additive	Impact modifier heat stabilizer
Features	Impact modification Low Temperature Flexibility Low temperature impact resistance Thermal Stability
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.17	g/cm³	ISO 1183
Molding Shrinkage ¹	0.90 - 1.8	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	1.8	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	4400	MPa	ISO 527-2
Tensile Stress	90.0	MPa	ISO 527-2
Tensile Strain (Break)	8.0	%	ISO 527-2
Flexural Modulus	3600	MPa	ISO 178
Flexural Stress	110	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	20	kJ/m²	ISO 179/1eA
Notched Izod Impact	22	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength	> 45	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	190	°C	ISO 75-2/B
1.8 MPa, not annealed	140	°C	ISO 75-2/A

Flammability	Nominal Value		Test Method
Flame Rating (1.50 mm, Teknor Apex test result)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	20	hr
Rear Temperature	250 - 280	°C
Middle Temperature	250 - 280	°C
Front Temperature	250 - 280	°C
Processing (Melt) Temp	250 - 290	°C
Mold Temperature	60.0 - 80.0	°C
Injection Rate	Fast
Back Pressure	Moderate
Screw Speed	Moderate

Injection instructions
No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	E4EPPX_Chemlon-MDF463.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Shandong PA6 A1R03	Shandong Dongchen Engineering Plastics Co., Ltd.	Nylon 6	Shandong PA6
NuSil R-2145	NuSil Technology	Silicone	NuSil
Badaflex® TPE-S 50D 1040	Bada AG	SEBS	Badaflex®
Daelim Po1y® LH-4100BL	DAELIM INDUSTRIAL CO., LTD.	HDPE	Daelim Po1y®
Hostacom EYS 349N	LyondellBasell Industries	PP Copolymer	Hostacom