PRL ABS-GP-IM
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E440X2_PRL-ABS-GP-IM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL ABS-GP-IM is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 7.0 to 11 | g/10 min | |
| 230°C/3.8 kg | 1.0 to 3.0 | g/10 min | |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 1930 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 37.9 | MPa | |
| Break, 3.18 mm | 30.4 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 2.0 | % | |
| Break, 3.18 mm | 25 | % | |
| Flexural Modulus (3.18 mm) | 1890 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 58.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 28 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 370 | J/m | ASTM D256 |
| -30°C | 9.0 | kJ/m² | ISO 180/1A |
| 23°C | 28 | kJ/m² | ISO 180/1A |
| Gardner Impact (3.18 mm) | 22.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 87.8 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 82.2 | °C | |
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 193 to 210 | °C | |
| Middle Temperature | 216 to 238 | °C | |
| Front Temperature | 227 to 254 | °C | |
| Processing (Melt) Temp | 232 to 274 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA6G13-BK10 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| Braskem PE SGE7252XP | Braskem America Inc. | HDPE | Braskem PE |
| HiFill® PEI BK | Techmer Engineered Solutions | PEI | HiFill® |
| KumhoSunny PC/ABS HAC8250Z | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| LUVOCOM® 50-8022 VP | Lehmann & Voss & Co. | PC | LUVOCOM® |