LNP™ LUBRICOMP™ UFL36AS compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E3WO3T_LNPLUBRICOMPUFL36AScompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP UFL36AS is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features include Internally Lubricated, Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound UFL-4036 A HS Product reorder name: UFL36AS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (340°C/2.16 kg) | 13.0 - 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 24 hours | 0.72 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.21 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 190 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 9200 | MPa | ISO 178 |
| 80°C | 8400 | MPa | ISO 178 |
| 100°C | 7600 | MPa | ISO 178 |
| 120°C | 5400 | MPa | ISO 178 |
| 150°C | 3800 | MPa | ISO 178 |
| 180°C | 3500 | MPa | ISO 178 |
| 200°C | 3100 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 251 | MPa | ISO 178 |
| 80°C | 214 | MPa | ISO 178 |
| 100°C | 194 | MPa | ISO 178 |
| 120°C | 141 | MPa | ISO 178 |
| 150°C | 97.0 | MPa | ISO 178 |
| 180°C | 82.0 | MPa | ISO 178 |
| 200°C | 71.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.48 | ASTM D3702 Modified | |
| With Self-Static | 0.52 | ASTM D3702 Modified | |
| Flexural Strain at Break 2 | ISO 178 | ||
| -- | 2.8 | % | ISO 178 |
| 80°C | 3.1 | % | ISO 178 |
| 100°C | 3.9 | % | ISO 178 |
| 120°C | 5.3 | % | ISO 178 |
| 150°C | 5.0 | % | ISO 178 |
| 180°C | 4.8 | % | ISO 178 |
| 200°C | 4.8 | % | ISO 178 |
| Wear Factor - Washer | 5.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -40°C 3 | 12 | kJ/m² | ISO 180/1A |
| 23°C 4 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -40°C | 45 | kJ/m² | ISO 180/1U |
| 23°C | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed, 64.0 mm Span) | 280 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 5.8E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1720 | J/kg/°C | ASTM E1269 |
| Thermal Conductivity | 0.24 | W/m/K | ASTM D5930 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 - 321 | °C | |
| Middle Temperature | 316 - 327 | °C | |
| Front Temperature | 327 - 338 | °C | |
| Processing (Melt) Temp | 316 - 332 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*3 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN G-152 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| SNOLEN® IM 31/54 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| Boda BDP-H9801 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Jampilen SP179 | Jam Polypropylene Company | PP Copolymer | Jampilen |
| Sylvin 5210-75 Orange 5109 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |