TECHNYL® B 230 GREY 1421 H
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E3LfPe_TECHNYLB230GREY1421H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® B 230 Grey 1421 H is an unfilled copolyamide 6.6/6, impact modified, for injection moulding. This product offers an excellent notched impact resistance, even at low temperature. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | 900 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Yield, 23°C | 65.0 | -- | MPa | ASTM D638 |
| Yield, 23°C | 60.0 | 45.0 | MPa | ISO 527-2/1A |
| Fracture, 23°C | 50.0 | 40.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ||||
| Yield, 23°C | 5.0 | 12 | % | ISO 527-2 |
| Fracture, 23°C | 70 | -- | % | ASTM D638 |
| Fracture, 23°C | 50 | 250 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 2400 | -- | MPa | ASTM D790 |
| 23°C | 2000 | 700 | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 85.0 | -- | MPa | ASTM D790 |
| 23°C | 80.0 | 27.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact | ||||
| 23°C | 140 | -- | J/m | ASTM D256 |
| 23°C | 7.0 | 18 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 62.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 242 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 5.0E+15 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 20 | 16 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | IEC 60112 | |||
| Solution a | 600 | 600 | V | IEC 60112 |
| Solution B | 475 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.6 mm) | HB | -- | UL 94 | |
| Oxygen Index | 21 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 255 - 265 | °C | |
| Front Temperature | 265 - 275 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® VE720 | A. Schulman Europe | ABS | RONFALIN® |
| Capilene® T 89 E | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| Exelene® LLDPE 1600 | Montachem International, Inc. | LLDPE | Exelene® LLDPE |
| Kuraray Poval® PVA 110 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| LNP™ LUBRICOMP™ LGL33 compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |