LNP™ THERMOCOMP™ KF002XXP compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E3GUd7_LNP-THERMOCOMP-KF002XXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP KF002XXP is a compound based on Acetal Copolymer resin containing 10% Glass Fiber. Added features of this material include: Chemically Coupled. Also known as: LNP* THERMOCOMP* Compound KFX-1002 Product reorder name: KF002XXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.2 | % | |
| Across Flow : 24 hr | 1.3 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4760 | MPa | ASTM D638 |
| -- | 5400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 84.1 | MPa | ASTM D638 |
| Break | 86.4 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.2 | % | ASTM D638 |
| Break | 3.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4620 | MPa | ASTM D790 |
| -- | 5400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 124 | MPa | ASTM D790 |
| -- | 137 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D4812 |
| 23°C 3 | 33 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 1.45 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 164 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 162 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 161 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 3314 | Formosa Plastics Corporation | LLDPE | TAISOX |
| TARFLON™ NEO ZG1950 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| AKROMID® A3 GK 30 1 natural (3673) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| ESPRENE EPDM 5527F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| Latamid 66 H2 G/50-GWHF1 | LATI S.p.A. | Nylon 66 | Latamid |