ENFLEX VU-424-75A
| Category: | PP+EPDM , Polypropylene + EPDM Rubber |
| Manufacturer: | Ravago Group |
| Trademark: | ENFLEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E332Z7_ENFLEX-VU-424-75A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Economical, vulcanized EPDM/PP series |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation (Break) | 670 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% Strain | 3.00 | MPa | |
| 300% Strain | 4.30 | MPa | |
| Tensile Stress (Break) | 9.60 | MPa | ISO 37 |
| Tear Strength | 48 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 24 | % | |
| 70°C, 22 hr | 49 | % | |
| 100°C, 22 hr | 83 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (125°C, 336 hr) | -6.5 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (125°C, 336 hr) | 540 | % | ISO 188 |
| Change in Shore Hardness in Air (Shore A, 125°C, 336 hr) | 5.0 4.0 | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -55.0 | °C | ISO 974 |
| Maximum Dynamic Service Temperature | 135 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman ABS 710 | Shuman Plastics, Inc. | ABS | Shuman ABS |
| HIDEN® HT306 | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| INELEC PA610CF30 | Infinity LTL Engineered Compounds | Nylon 610 | INELEC |
| LUVOCOM® 1/CF/40 | LEHVOSS Group | Nylon 66 | LUVOCOM® |
| ULTEM™ 2410EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |