Zytel® 70G13HS1L NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E1Ub6r_Zytel-70G13HS1L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 13% Glass Reinforced, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.23 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 0.70 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.7 | -- | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 7.6 | -- | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.2 | -- | % | ISO 62 |
| Viscosity Number | 150 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5500 | 3500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 13 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 3300 | MPa | |
| 1000 hr | -- | 2200 | MPa | |
| Flexural Modulus | 4900 | 2900 | MPa | ISO 178 |
| Flexural Stress | 190 | 100 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 4.5 | -- | kJ/m² | |
| -30°C | -- | 4.0 | kJ/m² | |
| 23°C | 5.0 | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 30 | 30 | kJ/m² | |
| 23°C | 32 | 70 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 4.5 | 3.0 | kJ/m² | |
| -30°C | 4.5 | 3.0 | kJ/m² | |
| 23°C | 4.5 | 4.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 35 | 28 | kJ/m² | |
| 23°C | 40 | 55 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 258 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 238 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 80.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 4.0E-5 | -- | cm/cm/°C | |
| Transverse | 9.6E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 7.0E-3 | 0.24 | ||
| 1 MHz | 7.0E-3 | 0.24 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.710 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Specific Heat Capacity of Melt | 2370 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.16 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Effective Thermal Diffusivity | 0.0850 | -- | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA/ABS Blend 3610/5 | TER HELL PLASTIC GMBH | Nylon 6+ABS | TEREZ PA/ABS |
| Ultralloy™ 910 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Chemlon® 243 GH | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Kingfa PBT JE2-R2 | Kingfa | ABS+PBT | Kingfa PBT |
| LNP™ LUBRICOMP™ Noryl_NWR5810 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |