UmaPET HSCO Datasheet,PET,Ester Industries Ltd.-SHANGHAI SUSHENG

Message
KEY FEATURES UmaPET HSCO is transparent film with one side heat sealable Co-extruded layer of special copolymer and other side corona treated. Corona treated side gives enhanced adhesion for printing and lamination. The special copolymer layer is design to heat seal onto itself as well as substrates such as APET, C-PET, Modified C-PET and A-PET coated boards. The film has excellent transparency, dimensional stability and barrier. The Film can be used for direct contact with food and complies with FDA regulation 21CFR177.1630 sections (f) and (g). APPLICATIONS Excellent in flexible packaging applications as sealant for products which need high aroma barrier like perfumed tissues, mosquito mats etc. Suitable for used in monolayer over wrap, temper evident packaging. Suitable for sealing cap liner for PET jars, see through lid for preformed PET trays, microoven able pouches for sandwich.

General Information
Features	Copolymer Food Contact Acceptable Good Adhesion Good Dimensional Stability Heat Sealable High Clarity
Uses	Film Food Wrap Liners Packaging Seals
Appearance	Clear/Transparent
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0120 mm	2.5	%
Flow : 150°C, 30 min, 0.0150 mm	2.5	%
Flow : 150°C, 30 min, 0.0200 mm	2.0	%
Flow : 150°C, 30 min, 0.0250 mm	2.0	%
Across Flow : 150°C, 30 min, 0.0120 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0150 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0200 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0250 mm	0.40	%

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
vs. Itself - Dynamic ¹	0.40
vs. Itself - Dynamic ²	0.40
vs. Itself - Dynamic ³	0.40
vs. Itself - Dynamic ⁴	0.38
vs. Itself - Static ⁵	0.48
vs. Itself - Static ⁶	0.48
vs. Itself - Static ⁷	0.48
vs. Itself - Static ⁸	0.48

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	12 15 20 25	µm
Film Thickness - Recommended / Available	12, 15, 20, 25 µm
Tensile Strength			ASTM D882
MD : Break, 12 µm	177	MPa
MD : Break, 15 µm	177	MPa
MD : Break, 20 µm	172	MPa
MD : Break, 25 µm	172	MPa
TD : Break, 12 µm	186	MPa
TD : Break, 15 µm	186	MPa
TD : Break, 20 µm	181	MPa
TD : Break, 25 µm	181	MPa
Tensile Elongation			ASTM D882
MD : Break, 12 µm	100	%
MD : Break, 15 µm	100	%
MD : Break, 20 µm	100	%
MD : Break, 25 µm	100	%
TD : Break, 12 µm	90	%
TD : Break, 15 µm	90	%
TD : Break, 20 µm	90	%
TD : Break, 25 µm	90	%
Yield			Internal Method
12.0 µm	59.5	m²/kg
15.0 µm	47.6	m²/kg
20.0 µm	35.7	m²/kg
25.0 µm	28.6	m²/kg

Additional Information	Nominal Value	Unit	Test Method
Wetting Tension			ASTM D2578
Corona side : 12.0 µm	52	dyne/cm
Corona side : 15.0 µm	52	dyne/cm
Corona side : 20.0 µm	52	dyne/cm
Corona side : 25.0 µm	52	dyne/cm
Plain side : 12.0 µm	44	dyne/cm
Plain side : 15.0 µm	44	dyne/cm
Plain side : 20.0 µm	44	dyne/cm
Plain side : 25.0 µm	44	dyne/cm

Optical	Nominal Value	Unit	Test Method
Haze			ASTM D1003
12.0 µm	3.0	%
15.0 µm	3.0	%
20.0 µm	3.5	%
25.0 µm	4.0	%

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	E1Kb75_UmaPET-HSCO.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Megalon® 143GL	Mega Polymers	Nylon 66	Megalon®
ULTEM™ HU2100 resin	SABIC Innovative Plastics	PEI	ULTEM™
APEX® 80-C131E-NT	Teknor Apex Company	PVC, Flexible	APEX®
Colorite 11 Series 7511	Colorite Polymers	PVC, Unspecified	Colorite 11 Series
Karina WHITE COLOR CONCENTRATE	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina