ResinDirect HIPS8UL
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | ResinDirect |
| Trademark: | ResinDirect |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E071lZ_ResinDirect-HIPS8UL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ResinDirect HIPS8UL is a High Impact Polystyrene material. It is available in North America. Important attributes of ResinDirect HIPS8UL are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 21.4 | MPa | |
| Break | 18.6 | MPa | |
| Tensile Elongation 2(Yield) | 45 | % | ASTM D638 |
| Flexural Modulus 3 | 1930 | MPa | ASTM D790 |
| Flexural Strength 4 | 40.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 77.8 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.9 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 2.5 mm/min |
| 4 . | 2.5 mm/min |
| 5 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DIGITALWAX® DM 220 | DWS Systems | Unspecified | DIGITALWAX® |
| ExxonMobil™ LDPE LD 150 Series | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Kingfa AP-202 | Kingfa | PP, Unspecified | Kingfa |
| PENTAMID B GV30 E H UV natural | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| CERTENE™ PBM-35 | Muehlstein | PP Impact Copolymer | CERTENE™ |