Derakane® 8084
| Category: | Vinyl Ester , Vinyl Ester |
| Manufacturer: | Ashland Performance Materials |
| Trademark: | Derakane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dz9ghl_Derakane-8084.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DERAKANE 8084 epoxy vinyl ester resin is an elastomer modified resin designed to offer increased adhesive strength, superior resistance to abrasion and severe mechanical stress, while giving greater toughness and elongation. DERAKANE 8084 resin is the resin of choice as a primer to prepare a substrate surface (steel or concrete) for application of a corrosion resistant lining. It exhibits outstanding adhesive strength on different types of steel, aluminium and concrete. APPLICATIONS AND USE DERAKANE 8084 resin has exhibited chemical resistance across a broad range of acids, bases and organic chemicals. DERAKANE 8084 resin can be used for RTM, hand-lay up, spray-up, filament winding and other industrial FRP applications. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Solution Viscosity | 360 | mPa·s | |
| Styrene Content | 40 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Volume Shrinkage | 8.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 30 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | |||
| -- | 75.8 | MPa | ASTM D638 |
| -- | 76.0 | MPa | ISO 527-2 |
| Tensile Elongation (Yield) | 8.0 - 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 3310 | MPa | ASTM D790 |
| -- | 3300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 131 | MPa | ASTM D790 |
| -- | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 480 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 82.2 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 82.0 | °C | ISO 75-2/A |
| Glass Transition Temperature | 115 | °C | ASTM D3418, ISO 11357-2 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Properties of clear casting at 25°C. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TW200F8 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Sylvin 8347-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Borealis PP RJ470MO | Borealis AG | PP Random Copolymer | Borealis PP |
| ELEVATE™ EF446 | Westlake Chemical Corporation | EVA | ELEVATE™ |
| Hostacom TRC 333N C13091 | LyondellBasell Industries | PP Copolymer | Hostacom |