Queo™ 0203

Category:	Plastomer , Ethylene-based Plastomer
Manufacturer:	Borealis AG
Trademark:	Queo™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Dz1OwO_Queo-0203.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Queo™ 0203 is an ethylene based octene plastomer produced using a metallocene catalyst in a solution polymerisation process.

Queo 0203 is a versatile blend partner for other polyolefins in cast film, extrusion and moulding applications, offering :

Unrivalled sealing properties

Outstanding toughness, puncture resistance and low temperature impact strength

Excellent polyolefin compatibility

Flexibility

High clarity

Applications:
Demonstrated applications include :

Seal layers in lamination and flexible barrier films

Specialty cast stretch applications

PP film toughness modification

Lap sealing to OPP

Halogen free flame retardant compounds

High clarity household articles

Soft foams

Additives:

Queo 0203 contains processing stabilizers.

General Information
Additive	Unspecified Stabilizer
Features	Flame Retardant Good Flexibility Good Toughness Halogen Free High Clarity
Uses	Film Foam
Processing Method	Cast Film Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.902	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	3.0	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance	> 1000	hr	ASTM D1693B

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	43		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break)	31.0	MPa	ISO 527-2/5A
Tensile Strain (Break)	820	%	ISO 527-2/5A
Flexural Modulus	72.0	MPa	ISO 178

Films	Nominal Value	Unit	Test Method
Secant Modulus - MD	65.0	MPa	ASTM D882
Dart Drop Impact (Blown Film)	> 32	g	ASTM D1709

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength (23°C)	No Break		ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746
Vicat Softening Temperature	80.0	°C	ISO 306/A
Melting Temperature (DSC)	96.0	°C	ISO 11357

Optical	Nominal Value	Unit	Test Method
Gloss (45°)	82		ASTM D2457
Haze	2.0	%	ASTM D1003A

Additional Information	Nominal Value	Unit	Test Method
Puncture Resistance	26.5	J/cm	Internal Method
Sealing Initial Temperature	80	°C	ASTM F88

Resin Grade	Manufacturer	Category	Trademark
ResMart Ultra Nylon 6 6	ResMart	Nylon 66	ResMart Ultra
TECHNYL® A 218W V30 NATURAL	Solvay Engineering Plastics	Nylon 66	TECHNYL® A
Stanyl® TW200F3	DSM Engineering Plastics	Nylon 46	Stanyl®
Cri-Line FKX-719-75	Cri-Tech, Inc.	Fluorelastomer	Cri-Line
LEXAN™ LUX7436C resin	SABIC Innovative Plastics	PC	LEXAN™