Network Polymers PP PPB 25 1202 TF20
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Network Polymers PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DyuiOo_Network-Polymers-PP-PPB-25-1202-TF20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Network Polymers PP PPB 25 1202 TF20 is a Polypropylene Copolymer (PP Copolymer) product filled with 20% talc. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Ash Content | 20 to 24 | % | ASTM D5630 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 23.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield) | 6.3 | % | ASTM D638 |
| Flexural Modulus 4 | 1540 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 180 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 109 | °C | |
| 0.45 MPa, Unannealed, 6.35 mm | 120 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PPC-20T Nat | PolyOne Corporation | PP Copolymer | Maxxam™ |
| ACCUTECH™ CP0436W40L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Elexar® EL-8451 | Teknor Apex Company | TPE | Elexar® |
| Kepamid® 1500SF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| Sylvin 9655-60 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |