| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DyIqmE_BraskemPEHT5303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HT5303 is a high density polyethylene, hexene copolymer, produced through Unipol® process and developed for the manufacturing of corrugated pipes. It exhibits an appropriate balance between stiffness, impact and stress cracking resistance, as well as a high resistance to oxidative degradation. Application: Corrugated pipes for energy and telecom cables protection and for drainage of roads and sports fields. Process: Pipe Extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.954 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.30 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 26 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 2.00mm, 10% Igepal, molded, F50 | 43.0 | hr | ASTM D1693 |
| 50°C, 2.00mm, 100% Igepal, molded, F50 | 168 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 30.0 | MPa | ASTM D638 |
| Fracture, molding | 33.0 | MPa | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 1140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 128 | °C | ASTM D648 |
| Vicat Softening Temperature | 66.0 | °C | ASTM D1525 1 |
| Oxidation Induction Time 2(200°C) | > 25 | min | ASTM D3895 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| NCLS 3 | > 24 | hr | ASTM F2136 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| 2 . | Compression Molded |
| 3 . | Compression Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® L 60040 | Reliance Industries Limited | HDPE | RELENE® |
| SLOVALEN® PH 72 T 20 | Plastcom | PP, Unspecified | SLOVALEN® |
| Karina COMP. PVC ORANGE. -E 600-DA-32/222-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ SCL36 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ LUBRICOMP™ |
| LNP™ LUBRICOMP™ ZL003 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |