LNP™ THERMOCOMP™ DB008ERP compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DyAEsh_LNPTHERMOCOMPDB008ERPcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DB008ERP is a compound based on Polycarbonate resin containing Glass Bead. Added features of this material include: Easy Molding, Mold Release. Also known as: LNP* THERMOCOMP* Compound DB-1008 EM MR Product reorder name: DB008ERP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.73 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.67 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3960 | MPa | ASTM D638 |
| Tensile Strength (Break) | 42.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.2 | % | ASTM D638 |
| Flexural Modulus | 3840 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 400 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 133 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LHF491NS | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Sylvin 2920-80 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| DENKA POVAL B-17 | Denka Company Limited | PVOH | DENKA POVAL |
| LNP™ LUBRICOMP™ KL003E compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| Plexar® PX2413 | LyondellBasell Industries | HDPE | Plexar® |