UBE Nylon 1022 C2 Datasheet,Nylon 6,UBE Engineering Plastics, S.A.-SHANGHAI SUSHENG

Message
UBE NYLON 1022 C2 is a high viscosity, nanocomposite-modified Polyamide 6, offering excellent barrier properties. The material is suitable for cast and air-cooled blown film production.

General Information
Filler / Reinforcement	Nanofiller
Features	Workability, good Definition, high Compliance of Food Exposure Viscosity, High Barrier resin
Uses	Films
Agency Ratings	FDA Food Exposure, Not Rated European food contact, not rated
Forms	Particle
Processing Method	Blow film cast film

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.15	g/cm³	ASTM D792

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With self-dynamics	0.30	ASTM D1894
With Self-Static	0.30	ASTM D1894

Films	Nominal Value	Unit	Test Method
Secant Modulus - MD (Cast Film)	1050	MPa	ASTM D882
Tensile Strength - MD			ASTM D882
Yield, extruded film	38.0	MPa	ASTM D882
Fracture, extruded film	100	MPa	ASTM D882
Tensile Elongation - MD (Fracture, Extruded Film)	450	%	ASTM D882

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	215	°C	DSC

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	ASTM D257

Optical	Nominal Value	Unit	Test Method
Gardner Gloss	140		ASTM D523
Haze	1.5	%	ASTM D1003

Additional Information
The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Oxygen Permeability, ASTM D3985: 24 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 3.54Extractable Content, JIS K6810: <1.00 wt%Water Vapor Permeability, JIS Z0208: 60 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 10.5 NPiercing Elongation, JAS P1019, Cast Film: 12 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <30 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <15 hole/0.04 m²

Additional Information

The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Oxygen Permeability, ASTM D3985: 24 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 3.54Extractable Content, JIS K6810: <1.00 wt%Water Vapor Permeability, JIS Z0208: 60 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 10.5 NPiercing Elongation, JAS P1019, Cast Film: 12 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <30 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <15 hole/0.04 m²

Resin Grade	Manufacturer	Category	Trademark
Tecomid® NB40 GR20 NL XA60	Eurotec Engineering Plastics	Nylon 6	Tecomid®
Solanyl® BP blend 40R	Rodenburg Biopolymers B.V.	Biodeg Polymers	Solanyl® BP blend
LARIPUR® LPR 70D60	COIM S.p.A.	TPU-Polyether	LARIPUR®
Kazan HDPE 293-284	Kazanorgsintez Joint Stock Company	HDPE	Kazan HDPE
Domamid HT™ 7720R43F4H3 Bk-1	Technical Polymers, LLC	Nylon 66	Domamid HT™

Category:	Nylon 6 , Polyamide 6
Manufacturer:	UBE Engineering Plastics, S.A.
Trademark:	UBE Nylon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Dy5e6S_UBE-Nylon-1022-C2.pdf
PRICE:	Order Products email sales@su-jiao.com