NOVAPOL® LF-0219-A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dx0zMH_NOVAPOL-LF-0219-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NOVAPOL®LF-0219-A is a low density polyethylene material,. This product is available in North America and is processed by film extrusion. NOVAPOL®The main features of the LF-0219-A are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 170 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 190 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 9.00 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 22.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 18.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 250 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 550 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm, Blown Film) | 160 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 160 | g | ASTM D1922 |
| TD : 38 µm, blown film | 150 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 37 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 15 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture 2(38.0 µm) | 180 | J/cm | Internal method |
| Film properties are typical of blown film extruded on a 1.5" extruder with 3" die and 35-mil die gap at a blow up ratio of 2.5:1, but are dependent upon operating conditions. |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SureSpec HS-080 | Genesis Polymers | PS (HIPS) | SureSpec |
| Xuchuan XCS-J130G | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Fainplast PVC RH 306/W | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| POCAN® B 3215 000000 | LANXESS GmbH | PBT | POCAN® |
| Sylvin 4280-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |