EL-Lene™ L2009FA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DvpxOq_EL-Lene-L2009FA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-LENE L2009FA is a butene LLDPE resin without Slip and Antiblocking agent. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 25% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693B |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 38 µm | 260 | MPa | |
| 2% Secant, TD : 38 µm | 272 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 11.8 | MPa | |
| TD : Yield, 38 µm | 13.7 | MPa | |
| MD : Break, 38 µm | 37.3 | MPa | |
| TD : Break, 38 µm | 34.3 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm | 620 | % | |
| TD : Break, 38 µm | 840 | % | |
| Dart Drop Impact (38 µm) | 130 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 150 | g | |
| TD : 38 µm | 370 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C | ASTM D2117 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (38.0 µm) | 53 | ASTM D2457 | |
| Haze (38.0 µm) | 15 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa ABS GR-20 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | ABS | Zhongfa |
| Hanwha Total PP FE17 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Hapflex™ 669-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Lucent PC GPCB-110 | Lucent Polymers, Inc. | PC+PBT | Lucent PC |
| LNP™ LUBRICOMP™ SFL2A compound | SABIC Innovative Plastics | Nylon 12 | LNP™ LUBRICOMP™ |