PRL PEI-GP1-TFE5
| Category: | PEI , Polyether Imide |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DvcZvF_PRL-PEI-GP1-TFE5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PEI-GP1-TFE5 is a Polyether Imide (PEI) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 5.0 to 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.18 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.1 | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.18 mm | 3450 | MPa | ASTM D638 |
| -- | 3280 | MPa | ISO 527-2/1 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 103 | MPa | |
| Break, 3.18 mm | 103 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 5.0 | % | |
| Break, 3.18 mm | 40 | % | |
| Flexural Modulus | |||
| 3.18 mm | 3380 | MPa | ASTM D790 |
| -- | 3030 | MPa | ISO 178 |
| Flexural Strength | |||
| 3.18 mm | 145 | MPa | ASTM D790 |
| -- 1 | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 53 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 53 | J/m | ASTM D256 |
| -30°C | 7.4 | kJ/m² | ISO 180/1A |
| 23°C | 8.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C, 3.18 mm) | 530 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (23°C, 3.18 mm) | 1200 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 2.26 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 204 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 196 | °C | |
| Vicat Softening Temperature | |||
| -- | 218 | °C | ASTM D1525 2 |
| -- | 214 | °C | ISO 306/B50 |
| -- | 209 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : 23 to 150°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : -20 to 150°C | 4.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 150°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -20 to 150°C | 4.0E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 143 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 338 to 399 | °C | |
| Mold Temperature | 107 to 177 | °C |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-1950-30A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| NOVADURAN® 5308F20 | Mitsubishi Engineering-Plastics Corp | PBT Alloy | NOVADURAN® |
| ELASTOSIL® N 9111 WHITE | Wacker Chemie AG | Silicone | ELASTOSIL® N |
| HiFill FR® PA6 GF/M45 L LE BK | Techmer Engineered Solutions | Nylon 6 | HiFill FR® |
| PLUSTEK RA320G3 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |