Generic TPO - Mineral
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DvFLpo_Generic-TPO---Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPO - Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.982 - 1.13 | g/cm³ | ASTM D792 |
| 23°C | 0.955 - 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 3.0 - 10 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 9.4 - 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.82 - 1.5 | % | ASTM D955 |
| 23°C | 0.55 - 1.2 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 60 - 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 16.5 - 30.7 | MPa | ASTM D638 |
| Yield, 23°C | 15.9 - 22.2 | MPa | ISO 527-2 |
| Fracture, 23°C | 12.0 - 20.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 5.0 - 100 | % | ASTM D638 |
| Fracture, 23°C | 20 - 500 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1220 - 3450 | MPa | ASTM D790 |
| 23°C | 1.80 - 1710 | MPa | ISO 178 |
| Flexural Strength (Yield, 23°C) | 15.7 - 46.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 - 50 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 25 - 490 | J/m | ASTM D256 |
| 23°C | 7.0 - 54 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 115 - 137 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 89.6 - 111 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 53.6 - 137 | °C | ISO 306 |
| CLTE - Flow | 4.0E-5 - 9.0E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 75.1 | °C | |
| Drying Time | 3.4 - 3.5 | hr | |
| Rear Temperature | 200 | °C | |
| Middle Temperature | 215 | °C | |
| Front Temperature | 215 | °C | |
| Nozzle Temperature | 220 | °C | |
| Processing (Melt) Temp | 215 - 216 | °C | |
| Mold Temperature | 49.6 - 50.0 | °C | |
| Back Pressure | 43.0 - 44.1 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPO - MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuang-Bang HC-5050 | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| ELEVATE™ EF522 | Westlake Chemical Corporation | EVA | ELEVATE™ |
| ESTADIENE 1515 HT | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Hanwha Total PE 4141W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| Sylvin 7833-80 Blue 8450 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |