Solef® 460/461
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Solef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Du6Lt6_Solef-460-461.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Solef® 460/461 PVDF homopolymer has high melt viscosity and is typically processed by extrusion. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.76 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/21.6 kg) | 10 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 1310 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C | 48.0 | MPa | |
| Break, 23°C | 41.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 23°C | 10 | % | |
| Break, 23°C | 100 | % | |
| Flexural Modulus 4(23°C) | 1520 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 23°C) | 55.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.20 | ||
| vs. Itself - Static | 0.30 | ||
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 8.00 | mg |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed | 127 | °C | |
| 1.8 MPa, Annealed | 88.0 | °C | |
| Glass Transition Temperature | -39.0 | °C | ASTM D4065 |
| Melting Temperature | 160 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 132 | °C | ASTM D3418 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1340 | J/kg/°C | ASTM D3418 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM D433 |
| Crystallization Heat | 46.0 | J/g | ASTM D3418 |
| Heat of Fusion | 46.0 | J/g | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 6(23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 3.18 mm) | 10 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 6.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Oxygen Index | 44 | % | ASTM D2863 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Refractive Index | 1.420 | ASTM D542 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (232°C, 100 sec^-1) | 2600 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 50 mm/min |
| 6 . | 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMVO | Arkema | Nylon 11 | Rilsan® |
| Sylvin 6208-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Latamid 6 H2 G/30-V0AF | LATI S.p.A. | Nylon 6 | Latamid |
| PENTAMID A L1 H black | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Sylvin 9600-40FU Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |