ENVIROPLAS® ENV08-NC870
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIROPLAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DteC1z_ENVIROPLAS-ENV08-NC870.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compounding - Injection Molding Grade, Excellent Processability, Good Chemical and Heat Resistance, Good Surface Appearance, Low Thermal Expansion, Outstanding Wear and Friction Performance. REACH/RoHS 2 Complaint No Colorant Version, NC870 = To Be Assigned 5 Digit Code Indicating Natural, Black, or Custom Color The ENV08 Series of Products Are Available With Mold Release, Heat and/or UV Stabilizers, Special Use Additives |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 74 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.8 to 2.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 50.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 60 | % | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength | 81.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Gardner Impact 1(23°C) | 36.2 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 151 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 53.3 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 216 to 238 | °C | |
| Middle Temperature | 216 to 238 | °C | |
| Front Temperature | 221 to 243 | °C | |
| Nozzle Temperature | 216 to 238 | °C | |
| Mold Temperature | 48.9 to 71.1 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | No Failure Energy |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLOY® MS-0100B-13 | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| Gallonprene® GP210-4006 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Lastilac SP G/17 | LATI S.p.A. | ABS | Lastilac |
| Jampilen RP210M | Jam Polypropylene Company | PP Random Copolymer | Jampilen |
| POLYblend PC/ABS 65FS LB | Polykemi AB | PC+ABS | POLYblend |