Generic PBT Alloy - Glass Fiber
| Category: | PBT Alloy , Polybutylene Terephthalate Alloy |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DstHGk_Generic-PBT-Alloy---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PBT Alloy - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.33 - 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage (23°C) | 0.28 - 0.76 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.070 - 0.093 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6960 - 10700 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 109 - 137 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 - 2.6 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5000 - 12000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 100 - 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 - 60 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 6.0 - 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 210 - 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 168 - 192 | °C | ISO 75-2/A |
| Melting Temperature | 224 - 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.0E-5 - 3.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.9E-5 - 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 130 - 140 | °C | UL 746 |
| RTI Imp | 125 - 130 | °C | UL 746 |
| RTI | 120 - 132 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 - 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 - 2.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 20 - 40 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 3.55 | IEC 60250 | |
| Dissipation Factor (23°C) | 3.0E-3 - 0.017 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 6.5 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 240 | °C | |
| Front Temperature | 255 | °C | |
| Nozzle Temperature | 250 - 255 | °C | |
| Mold Temperature | 79.9 - 90.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PBT Alloy - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ PC-10CF/000 FR V0 BK035 | PolyOne Corporation | PC | Stat-Tech™ |
| TPC PVC SG840 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Generic SBS | Generic | SBS | Generic |
| KRATON® D1163 B | Kraton Polymers LLC | SIS | KRATON® |
| Sylvin 9077-94 Grey 9599 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |