OPNYL OP6GF33
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | OPNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DsfcKZ_OPNYL-OP6GF33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 6 - Glass reinforced (33 %), high tensile strength, stiffness and HDT. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.40 | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.15 to 0.25 | 0.15 to 0.25 | % | ASTM D955 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1 | 9000 | 6900 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 180 | 110 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 | 5.5 | % | ASTM D638 |
| Flexural Modulus 4 | 9100 | 5400 | MPa | ASTM D790 |
| Flexural Strength 5(Yield) | 230 | 170 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | 130 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Annealed, 3.20 mm | 216 | -- | °C | |
| 1.8 MPa, Annealed, 3.20 mm | 208 | -- | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultron® 150C6 | Asia International Enterprise (Hong Kong) Limited | PEI | Ultron® |
| DOWLEX™ 2344 | The Dow Chemical Company | PE Copolymer | DOWLEX™ |
| POLLITE 1001 | POLYROCKS CHEMICAL CO., LTD | PC | POLLITE |
| Hifax TRC 221X BLACK | LyondellBasell Industries | PP Copolymer | Hifax |
| Hifax TRC 770X LC GRY | LyondellBasell Industries | TPO (POE) | Hifax |