Kingfa PA6-RG001
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DsPxRK_Kingfa-PA6-RG001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PA6-RG001 is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa PA6-RG001 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 1.1 to 1.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.4 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 16 | % | ASTM D638 |
| Flexural Modulus 3 | 2300 | MPa | ASTM D790 |
| Flexural Strength 4 | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 185 | °C | |
| 1.8 MPa, Unannealed | 55.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2656 | Covestro - Polycarbonates | PC | Makrolon® |
| SWANCOR Epoxy 905-2 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| ULTEM™ HU2210 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| LEXAN™ HFD1810 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| OxyVinyls® 500F | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |