Retpol® PDR 1619/4 HS
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DsMfZg_Retpol-PDR-1619-4-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Corton PDR 1619/4 HS is a 11% barium sulphate filled homopolymer polypropylene compound. It is a high flow injection moulding grade developed for high gloss appliance applications requiring improved rigidity and greater dimensional stability than provided by unfilled grades. It has been stabilized for continuous use at elevated temperature. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.988 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 28 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.4 to 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 100 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 77 | ||
| Shore D, 15 sec, 3.00 mm | 68 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 33.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 88 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 1740 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 25 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 570 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 116 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 55.0 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PP PGF6301 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| Sindustris PBT GP2077F | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| ASTALOY™ ASA/PET MDA256 | Marplex Australia Pty. Ltd. | ASA+PET | ASTALOY™ |
| Eastar™ DN004HF | Eastman Chemical Company | Copolyester | Eastar™ |
| EMPILON® 345 | EMPILON | SEBS | EMPILON® |