LNP* STAT-KON* LX00486C is a compound based on Polyetheretherketone containing proprietary fillers. Added features of this grade includes: Clean Compound System, Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-L-00486 CCS Product reorder name: LX00486C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.25 | % | |
| Across Flow : 24 hr | 1.3 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.050 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 17300 | MPa | ASTM D638 |
| -- | 16300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 179 | MPa | ASTM D638 |
| Break | 177 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.0 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 13600 | MPa | ASTM D790 |
| -- 5 | 13500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 255 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 262 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 63 | J/m | ASTM D256 |
| 23°C 7 | 5.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 660 | J/m | ASTM D4812 |
| 23°C 8 | 40 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.80 | J | ASTM D3763 |
| -- | 2.34 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 336 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 330 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 315 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 291 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 to 1.0E+7 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| En Chuan 332 | En Chuan Chemical Industries Co,. Ltd. | PS (GPPS) | En Chuan |
| Eltex® PF6212AA | INEOS Olefins & Polymers Europe | mLLDPE | Eltex® |
| LubriOne™ PC-20GF/15T | PolyOne Corporation | PC | LubriOne™ |
| Petlon Prime A1-00-00-NT | Petlon Polymers Ltd | Nylon 66 | Petlon Prime |
| Thermec N™ 4340R45F4 | Technical Polymers, LLC | PPA | Thermec N™ |