OmniLon™ PA6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniLon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Drl1pe_OmniLon-PA6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection Molding Grade, Nylon 6 |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.1 to 1.6 | % | |
| Across Flow | 1.1 to 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 79.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 107 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 177 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 65.6 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 232 to 271 | °C | |
| Middle Temperature | 238 to 271 | °C | |
| Front Temperature | 238 to 271 | °C | |
| Nozzle Temperature | 249 to 282 | °C | |
| Processing (Melt) Temp | 232 to 271 | °C | |
| Mold Temperature | 26.7 to 82.2 | °C | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2740 S-90A | RTP Company | SEBS | RTP |
| Gallonprene® GP520-7504 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Huafon HF-3495A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Iupital® FT2020 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| OTECH PVC OW135 - Automotive Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |