Menzolit® SMC 0300 Datasheet,Polyester, TS,Menzolit Ltd (UK)-SHANGHAI SUSHENG

Menzolit® SMC 0300

Category:	Polyester, TS , Thermoset Polyester
Manufacturer:	Menzolit Ltd (UK)
Trademark:	Menzolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Dr6qd2_Menzolit-SMC-0300.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Menzolit® SMC 0300 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® SMC 0300 is a low shrink standard SMC providing improved surface quality, reduced shrinkage and warpage. Typical fields of applications are mechanical engineering and electrical industry, where improved dimensional stability and better surface properties are required, e.g. seat shells, covers or functional components. The flammability meets the demands of standard UL 94 category HB. Despite the low shrinkage, a homogeneous pigmentation is possible. The glass content has been adjusted to a level combining good mouldability with good mechanical properties.

Message

Menzolit® SMC 0300 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens.

Menzolit® SMC 0300 is a low shrink standard SMC providing improved surface quality, reduced shrinkage and warpage. Typical fields of applications are mechanical engineering and electrical industry, where improved dimensional stability and better surface properties are required, e.g. seat shells, covers or functional components. The flammability meets the demands of standard UL 94 category HB. Despite the low shrinkage, a homogeneous pigmentation is possible. The glass content has been adjusted to a level combining good mouldability with good mechanical properties.

General Information
Filler / Reinforcement	Glass\Mineral, 27% Filler by Weight
Features	Flame Retardant Good Dimensional Stability Good Moldability Good Surface Finish Halogen Free High Heat Resistance Low Shrinkage Low Smoke Emission Low Warpage
Uses	Electrical/Electronic Applications Engineered Applications
Appearance	Colors Available
Forms	SMC - Sheet Molding Compound
Processing Method	Compression Molding
Part Marking Code (ISO 11469)	>UP-(MD+GF)69<

Physical	Nominal Value	Unit	Test Method
Density	1.70	g/cm³	ISO 1183
Molding Shrinkage
-- ¹	0.0	%	DIN 53464
--	0.080	%	ISO 2577
Water Absorption (Saturation, 23°C)	< 0.50	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Compression Molded)	12000	MPa	ISO 527-2
Tensile Stress (Yield, Compression Molded)	64.0	MPa	ISO 527-2
Flexural Modulus (Compression Molded)	10000	MPa	ISO 178
Flexural Stress (Compression Molded)	154	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (Compression Molded)	70	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	> 200	°C	ISO 75-2/A
Continuous Use Temperature	165	°C	Internal Method
Glass Transition Temperature	170	°C	DSC
CLTE - Flow	1.2E-5	cm/cm/°C	ISO 11359-2

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+12	ohms	IEC 60093
Volume Resistivity	1.0E+15	ohms·cm	IEC 60093
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (3.00 mm)	HB		UL 94
Glow Wire Ignition Temperature	750	°C	IEC 60695-2-13
Oxygen Index	22	%	ISO 4589-2

Additional Information	Nominal Value		Test Method
Glow Bar	Level BH 2 <= 95		IEC 60707-3

Injection	Nominal Value	Unit
Mold Temperature	135 to 150	°C
Injection Pressure	8.00 to 10.0	MPa

Note Message
1 .	Post Molding Shrinkage

Resin Grade	Manufacturer	Category	Trademark
Celanex® 531HS	Celanese Corporation	PBT	Celanex®
EMAREX® 300 GF43	MRC Polymers, Inc.	Nylon 6	EMAREX®
EnCom ABS 3535	EnCom, Inc.	ABS	EnCom
K-Prene GHT 75	Technovinyl Polymers India Ltd.	TPE	K-Prene
Sylvin 8865-75FUV Grey 9518	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin

Resin Grade

Manufacturer