Geon™ Vinyl Flexible A7001
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Flexible |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DqK5z6_Geon-Vinyl-Flexible-A7001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Interior compound used primarily in transparent applications. This product is registered under UL 94 HB specifications @ 3.0 and 1.5 mm. thickness and all colors. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.9 to 2.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 70 | ||
| Shore A, 15 sec | 59 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Break | 11.0 | MPa | |
| 100% Strain | 4.55 | MPa | |
| Tensile Elongation 2(Break) | 450 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 3 | 40.3 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 18 | % | ASTM D395 |
| Clash-Berg Modulus | ASTM D1043 | ||
| -- | 37.2 | MPa | |
| -52°C | 310 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -51.1 | °C | ASTM D746 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 4(1910 µm) | 82.0 | % | ASTM D1003 |
| Haze (1910 µm) | 4.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 193 to 204 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 171 to 177 | °C |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | Die C, 510 mm/min |
| 4 . | CIE Illuminant C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLUX® (MABS) Typ C2 | A. Schulman Europe | MABS | POLYLUX® |
| Shandong Aobang TPU-Capro 95-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Capro | Shandong Aobang TPU-Capro |
| STAR-THERM® E A-3C | EPIC Polymers | Nylon 66 | STAR-THERM® |
| ULTEM™ 1000E resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| LNP™ STAT-KON™ DX13315C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |