Celstran® PP-GF50-0403 P10/10
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DqG2wC_Celstran-PP-GF50-0403-P10-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Material code according to ISO 1043-1: PP Heat stabilized polypropylene reinforced with 50 weight percent long glass fibers. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 12000 | MPa | ISO 527-2/1A/1 |
| 80°C | 8400 | MPa | ISO 527-2/1A |
| Tensile Stress | |||
| Fracture | 140 | MPa | ISO 527-2/1A/5 |
| 80°C | 85.0 | MPa | ISO 527-2/1A |
| Tensile Strain | |||
| Fracture | 1.8 | % | ISO 527-2/1A/5 |
| Fracture, 80°C | 2.3 | % | ISO 527-2/1A |
| Flexural Modulus | ISO 178 | ||
| 23°C | 12000 | MPa | ISO 178 |
| 80°C | 8500 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 220 | MPa | ISO 178 |
| 80°C | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 31 | kJ/m² | ISO 179/1eA |
| 23°C | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 64 | kJ/m² | ISO 179/1eU |
| 23°C | 66 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 158 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 134 | °C | ISO 75-2/C |
| Melting Temperature 1 | 165 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 260 - 270 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Nozzle Temperature | 280 - 290 | °C | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 260 to 290°CZone 4 Temperature: 280 to 290°CFeed Temperature: 20 to 50°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC6MLZ (Series: AD1) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Clariant Nylon 6/6 66G43-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Conpol™ 13B | DuPont Packaging & Industrial Polymers | EMAA | Conpol™ |
| Karina CLEAR PVC COMPOUND 57/201-D-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 6185-80 Grey 945 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |