SABIC® PC FL405 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Doyb95_SABIC-PC-FL405-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Various weight reductions at 0.250" (6.38 mm) wall. Impact resistant, superior processing, excellent surface. UL94 V-0 at 0.120 |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.08 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (6.40 mm) | 0.60 - 0.80 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.14 | % | ASTM D570 |
| Equilibrium, 23°C | 0.31 | % | ASTM D570 |
| Foam - Physical 2 | 10 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Mechanical 3 | 10 | % | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Impact 4 | 10 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Thermal 5 | 10 | % | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Electrical 6 | 20 | % | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Flame Class Minimum Density | 1.060 | g/cm³ | Internal method |
| Radiant Panel Listing (UL) | YES |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (6.40 mm) | 2100 | MPa | ASTM D638 |
| Tensile Strength (Yield, 6.35 mm) | 54.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 6.35 mm) | 7.2 | % | ASTM D638 |
| Flexural Modulus (6.40 mm) | 2480 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 2700 | J/m | ASTM D4812 |
| Dart Drop Impact (23°C) | 61.0 | J | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 127 | °C | ASTM D648 |
| CLTE - Flow (-40 to 95°C) | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1340 | J/kg/°C | ASTM C351 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.1E+17 | ohms | ASTM D257 |
| Volume Resistivity | 3.5E+17 | ohms·cm | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 2.42 | ASTM D150 | |
| 1 MHz | 2.43 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 1.1E-3 | ASTM D150 | |
| 1 MHz | 4.4E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.05 mm | V-0 | UL 94 | |
| 6.10 mm | 5VA | UL 94 | |
| Oxygen Index | 39 | % | ASTM D2863 |
| Additional Information |
|---|
| Structural Foam Molding - Blowing Agent, Chemical System: FLC298Structural Foam Molding - Blowing Agent, Physical System: Nitrogen GasStructural Foam Molding - Concentration Range (Blowing Agent): 3 - 5 %Structural Foam Molding - Drying Temperature (Blowing Agent): 104 °CStructural Foam Molding - Drying Temperature (Resin): 121 °CStructural Foam Molding - Drying Time (Blowing Agent): 4 hrsStructural Foam Molding - Drying Time (Resin): 3 - 4 hrsStructural Foam Molding - Drying Time (Resin, Cumulative): 48 hrsStructural Foam Molding - Front Temperature: 277 - 299°CStructural Foam Molding - Melt Temperature: 274 - 299 °CStructural Foam Molding - Middle Temperature: 277 - 299 °CStructural Foam Molding - Mold Temperature: 71 - 93 °CStructural Foam Molding - Nozzle Temperature: 265 - 288 °CStructural Foam Molding - Rear Temperature: 271 - 293 °CStructural Foam Molding - Recommended Concentration (Blowing Agent): 1.5 % |
| Note Message | |
|---|---|
| 1 . | Foam molded |
| 2 . | 6.4 mm wt reduction |
| 3 . | 6.4 mm wt reduction |
| 4 . | 6.4 mm wt reduction |
| 5 . | 6.4 mm wt reduction |
| 6 . | 6.4 mm wt reduction |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CP PRYME® Polycarbonate PC300 BK | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Galloo GP-PE-110 | Galloo Plastics | PE, Unspecified | Galloo |
| Hanwha Total PP BI961 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| LG PMMA ID188 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| HIFOR Xtreme® SC74871 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |