| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOCETAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DoaLS2_KOCETAL-GF706.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kocetal GF706 is glass fiber reinforced grade for high strength and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (Equilibrium, 60% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 150 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 6.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8200 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 165 | °C | |
| 1.8 MPa, Unannealed | 164 | °C | |
| Peak Melting Temperature | 166 | °C | ASTM D1525 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.70 | ASTM D2520 | |
| Dissipation Factor (1 MHz) | 6.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 702 | RTP Company | HDPE | RTP |
| TECHNYL® C 548B V15 BLACK | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Abstron IM17 SHG | Bhansali Engineering Polymers Limited | ABS+Acrylic | Abstron |
| Daelim Po1y® PP-245 | DAELIM INDUSTRIAL CO., LTD. | PP Impact Copolymer | Daelim Po1y® |
| Lion Idemitsu Composites PPS K521A2 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |