Cereplast Compostables® 1013
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Cereplast, Inc. |
| Trademark: | Cereplast Compostables® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Do39W4_Cereplast-Compostables-1013.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cereplast Compostables® resins are renewable, ecologically sound substitutes for petroleum-based plastic product, replacing nearly 100% of the petroleum-based additives used in traditional plastics. Cereplast Compostables® resins are using polymer and additives derived from starch and other renewable resources chemistry. These components are carefully blended together on state-of-the-art compounding equipments. All Cereplast Compostables® resins, including Compostable 1013, are certified as biodegradable and compostable in the United States and Europe, meeting BPI (Biodegradable Products Institute www.bpiworld.com) standards for compostability (ASTM6400D99, ASTM6868) and European Bioplastics Standards (EN13432). Compostable 1013 has been designed to have an excellent balance of low stiffness, toughness, and processability. Compostable 1013 can be processed on existing conventional electric and hydraulic reciprocating screw injection molding machines. Please see our processing guide for processing and material drying guidelines. This can be found at www.cereplast.com. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 972 | MPa | ASTM D638 |
| Tensile Strength (Break) | 21.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 350 | % | ASTM D638 |
| Flexural Modulus | 703 | MPa | ASTM D790 |
| Flexural Strength | 18.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 34 | J/m | ASTM D256 |
| 23°C | 420 | J/m | ASTM D256 |
| Dart Drop Impact | 18.1 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -35.0 | °C | ASTM D746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 163 - 177 | °C | |
| Middle Temperature | 177 - 191 | °C | |
| Front Temperature | 177 - 204 | °C | |
| Nozzle Temperature | 177 - 204 | °C | |
| Processing (Melt) Temp | 174 - 204 | °C | |
| Mold Temperature | 10.0 - 26.7 | °C | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| Material Drying Temp (regrind): 100 to120°F (4 hrs.) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CompaMid® PA 6 GK 30 | DimeLika Plast GmbH | Nylon 6 | CompaMid® |
| ICORENE® N2303 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| IPC PP 4840C-C | International Polymers Corporation | PP Copolymer | IPC PP |
| OnForce™ LFT LFT PP-30 LGF/000 1001 | PolyOne Corporation | PP Homopolymer | OnForce™ LFT |
| POFEX EP8004S150F | POLYROCKS CHEMICAL CO., LTD | XLPE | POFEX |