GETILAN GPE/410 AF
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DncVHL_GETILAN-GPE-410-AF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GETILAN is the trade-mark of our crosslinkable polythene. GETILAN GPE/410 AF is a chemically crosslinkable low smoke and low toxicity halogen free flame retardant compound for insulation and sheathing. It is a conveniently grafted polythene able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/100 PSF. Where and when anti-ageing and anti-copper functions are required, we suggest our type MAC/202 or MAC/308 PSL (less in reaction). REACTION BETWEEN GRAFTING AND CATALYST These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 97 / 3 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 3.0 - 8.0 | g/10 min | ASTM D1238 |
| Water absorption rate- 24 hr (100°C) | 6.00 | g/m² | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811 | ||
| 200°C | 30 | % | IEC 60811 |
| Residual : 200°C | 0.0 | % | IEC 60811 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | 0 | % | IEC 60754-1 |
| Corrosive gases in flue gas- pH | > 4.30 | IEC 60754-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 17.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 240 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (155°C, 168 hr) | 8.0 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (155°C, 168 hr) | -16 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | BS 6622 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 25 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 205 | °C | |
| Die Temperature | 215 | °C |
| Extrusion instructions |
|---|
| Crosslinking of the finished product is obtained by: Immersion of the bobbin in hot water at 85/90°C for two hours (up to 3 mm thickness) Steam treatment at 0.15 bar for 5/6 hours. |
| Note Message | |
|---|---|
| 1 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 202A GB 15 | RTP Company | Nylon 6 | RTP |
| Sindustris POM HI521 | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| Axiall PVC LSS-8200 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| KOCETAL® WR301RD | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| I. Stern 550 | I. STERN & CO. INC. | PS (HIPS) | I. Stern |