DIALAC® E259B
| Category: | SAS , Styrene Acrylonitrile Silicone Copolymer |
| Manufacturer: | UMG ABS, Ltd. |
| Trademark: | DIALAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DnVt2C_DIALAC-E259B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DIALAC® E259B is a Styrene Acrylonitrile Silicone Copolymer (SAS) material. It is available in Asia Pacific or North America. Primary attribute of DIALAC® E259B: RoHS Compliant. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 109 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2450 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 46.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2700 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 2.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next ABS SXT4-02ABK | Next Polymers Ltd. | ABS | Next ABS |
| ARCEL® ULV (1.25 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| CELLOMER® 3000 | Microcell Composite Company | SBS | CELLOMER® |
| Elastollan® C 60 D | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Polifor® 10 TE/30 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |