Huafon JF-P-6765 / JF-I-6722
| Category: | PUR-Ester , Polyurethane (Polyester based) |
| Manufacturer: | Huafon Group Co., Ltd. |
| Trademark: | Huafon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dn1utW_Huafon-JF-P-6765-JF-I-6722.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characteristic: Medium to low hardness. high fluidity. Application: For casual shoes and sport shoes. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density 1 | 0.550 to 0.600 | g/cm³ |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Hardness | |||
| Asker A : 23°C | 40.0 to 45.0 | ||
| Asker C : 23°C | 65.0 to 70.0 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 78 to 80 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color 2 | Clear/Transparent | ||
| Density | |||
| 40°C 3 | 1.14 to 1.18 | g/cm³ | |
| 40°C 4 | 1.18 to 1.20 | g/cm³ | |
| Viscosity | |||
| 40°C 5 | 0.10 to 0.30 | Pa·s | |
| 40°C 6 | 0.80 to 1.2 | Pa·s |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | > 6.00 | MPa | |
| Tensile Elongation at Break | > 400 | % | |
| Tear Strength | > 20.0 | kN/m |
| Note Message | |
|---|---|
| 1 . | Molded Density |
| 2 . | Part B |
| 3 . | Part A |
| 4 . | Part B |
| 5 . | Part B |
| 6 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riblene® FM 34 F | Versalis S.p.A. | LDPE | Riblene® |
| Spartech Polycom PE4000 B2 | Spartech Polycom | HDPE, HMW | Spartech |
| Larpeek 10 GCE/600 | LATI S.p.A. | PEEK | Larpeek |
| LNP™ THERMOCOMP™ NX10302 compound | SABIC Innovative Plastics Asia Pacific | PC+ABS | LNP™ THERMOCOMP™ |
| Plenco 08218 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |