LUBEXAN 1522 NATURAL
| Category: | PC , Polycarbonate |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEXAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dml8WY_LUBEXAN-1522-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on Polycarbonate. Second choice. Medium viscosity. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 to 1.21 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 to 22 | g/10 min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.15 | % | |
| Saturation, 23°C, 3.20 mm | 0.36 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 to 3000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 60.0 to 70.0 | MPa | |
| Break | 45.0 to 55.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 7.0 to 12 | % | |
| Break | 25 to 30 | % | |
| Flexural Modulus 1 | 2000 to 2500 | MPa | ISO 178 |
| Flexural Stress 2 | 55.0 to 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength 3(23°C) | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 130 to 140 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 135 to 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 125 to 135 | °C | ASTM D648 |
| Glass Transition Temperature | 140 to 150 | °C | Internal Method |
| Vicat Softening Temperature | |||
| -- | 135 to 145 | °C | ISO 306/A120 |
| -- | 130 to 140 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 850 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-HO-HF-40T | Pro Polymers | PP Homopolymer | Pro-Comp™ |
| Novalloy-B B27B6 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| APEX® 94-A0098C-90 | Teknor Apex Company | PVC, Flexible | APEX® |
| SQUARE® SFR1970-70 | Shenzhen SQUARE Silicone Co., Ltd. | Fluoro Si | SQUARE® |
| Sylvin 4260-75UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |