Celanex® 2004-2
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DmCsS2_Celanex-2004-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 2004-2 is an unfilled polyester that has an excellent combination of flowability and toughness. A typical application for Celanex 2004-2 is electrical connectors containing latches. Celanex 2004-2 contains an internal lubricant. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 33.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 1.8 - 2.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 53.1 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield, 23°C | 3.9 | % | ASTM D638 |
| Yield | 8.0 | % | ISO 527-2/1A/50 |
| Fracture, 23°C | 180 | % | ASTM D638 |
| Nominal Tensile Strain at Break | 37 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 69.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.5 | kJ/m² | ISO 179/1eA |
| 23°C | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | ISO 179/1eU |
| 23°C, local fracture | 220 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 4.6 | kJ/m² | ISO 180/1A |
| 23°C | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 166 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 162 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 56.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 54.0 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 60.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 175 | °C | ISO 306/B50 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3, ASTM D3418 |
| CLTE - Flow | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.2E+17 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength 3 | 15 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 1 MHz | 3.33 | ASTM D150 | |
| 100 Hz | 3.70 | IEC 60250 | |
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.021 | ASTM D150, IEC 60250 | |
| 100 Hz | 3.0E-3 | IEC 60250 | |
| Arc Resistance | 181 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Argothane® ST-2592-90 | Argotec LLC | TPU, Unspecified | Argothane® |
| Delrin® 327UVE NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Europrene® N 2860 | Versalis S.p.A. | NBR | Europrene® |
| KUBE PIR 22403 | KUBE Electronics AG | HDPE | KUBE PIR |
| Kazan LDPE 15313-003 OKP 22 1111 2003 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |