Infino HR-1008B
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DlLQDM_Infino-HR-1008B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS material that can be used for hand phone and car phone |
| General Information | |
|---|---|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 60 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 114 | ASTM D785 | |
| R-Scale | 117 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2700 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2/50 |
| Break 3 | 62.0 | MPa | ASTM D638 |
| Break | 47.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 100 | % | ASTM D638 |
| Break | 47 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2600 | MPa | ASTM D790 |
| -- 6 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 86.0 | MPa | ASTM D790 |
| -- 8 | 87.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 79 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 490 | J/m | ASTM D256 |
| 23°C 10 | 94 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 122 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 105 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 103 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 119 | °C | ISO 306/B50 |
| -- | 121 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| 6.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 100 | °C | |
| Desiccant Dryer | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 93.2 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech A707GH | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon, Unspecified | Sup-tech |
| YUNGSOX® PP 5018T | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| Braskem PP 6D83K | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| Braskem PE ML3600S | Braskem | LLDPE | Braskem PE |
| EPO-TEK® 730-110 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |