Arlon® 1263
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Greene, Tweed & Co. |
| Trademark: | Arlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Di6aSt_Arlon-1263.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arlon® 1263 is a Polyetheretherketone (PEEK) product filled with carbon fiber. It can be processed by injection molding and is available in Europe or North America. Typical application: Military Applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 108 | ASTM D785 | |
| Durometer Hardness (Shore D) | 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 0.5% Secant | 21700 | MPa | ASTM D638 |
| Tensile Strength (Break) | 230 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.9 | % | ASTM D638 |
| Flexural Modulus - 0.5% Secant | 19000 | MPa | ASTM D790 |
| Flexural Strength | 347 | MPa | ASTM D790 |
| Compressive Strength 1 | 262 | MPa | ASTM D695 |
| Shear Strength | ASTM D732 | ||
| -- 2 | 95.8 | MPa | |
| -- 3 | 120 | MPa | |
| Coefficient of Friction 4(vs. Itself - Dynamic) | 0.18 | ASTM G77 | |
| Deformation Under Load | 0.0600 | % | ASTM D621 |
| Wear Factor | 460 | 10^-8 mm³/N·m | ASTM G77 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 316 | °C | ASTM D648 |
| CLTE - Flow | ASTM D696 | ||
| < 149°C | 1.3E-5 | cm/cm/°C | |
| > 149°C | 3.1E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | at Break |
| 2 . | Transverse |
| 3 . | Axial |
| 4 . | PV = 12600 psi-ft/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A 38 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| SCHULADUR® A3 GF 30 SF SCHWARZ | A. Schulman Europe | PBT+ASA | SCHULADUR® |
| Hostalen ACP 7740 F2 | LyondellBasell Industries | HDPE | Hostalen |
| HOPELEX PC-1070S | Lotte Chemical Corporation | PC | HOPELEX |
| NILAMID® XS3 GF50/FA | Nilit Plastics | Nylon, Unspecified | NILAMID® |