Propafoil™ RVG120
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafoil™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Di09ae_Propafoil-RVG120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Metallized Film Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with polyolefinic polymers and subsequently metallized on one surface. RVG120 is particularly suited to form-film-seal packaging of confectionery, bakery items, ice-cream and grocery products. The metallized surface provides an excellent barrier to UV/visible light, retards rancidity, extends shelf-life and prevents show through of the packaged product. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density - Optical | 2.20 | BS 4432 | |
| Shrinkage | Internal Method | ||
| MD, 60secs : 129°C | 6.0 | % | |
| TD, 60secs : 129°C | -1.0 | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Corona Treatment | 38 | dyne/cm | Internal Method |
| Yield | 36.7 | m²/kg | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction 1 | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.50 | ||
| vs. Itself - Static | 0.50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 3000 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 2690 | MPa | |
| 1% Secant, TD | 2290 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield | 239 | MPa | |
| TD : Yield | 190 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break | 90 | % | |
| TD : Break | 130 | % | |
| Seal Strength 4 | 0.14 | N/mm | Internal Method |
| Seal Initiation Temperature 5 | 116 to 146 | °C | Internal Method |
| Oxygen Permeability (23°C, 0% RH) | 3.5 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 0.93 | g/m²/24 hr | ASTM F1249 |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Transmittance 6 | < 1.0 | % |
| Note Message | |
|---|---|
| 1 . | Film to Film, Non-Metallized Surface |
| 2 . | 50%/min |
| 3 . | 50%/min |
| 4 . | 225°F; 1sec; 15lb/in²; non-metallized surface |
| 5 . | 2secs; 15lb/in²; non-metallized surface |
| 6 . | UV/Visible |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207D TFE 15 | RTP Company | Nylon 612 | RTP |
| Nypol® PA A3 G50 NTLA010 NR308 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| AIE PET 40G3F | Asia International Enterprise (Hong Kong) Limited | PET | AIE PET |
| Generic PP Copolymer - Mineral | Generic | PP Copolymer | Generic |
| Edistir® N 3840 | Versalis S.p.A. | PS (GPPS) | Edistir® |