Pyramid™ PEEK KD2000 CAM Tube
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Pyramid™ PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dhd0C2_Pyramid-PEEK-KD2000-CAM-Tube.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyetheretherketone (PEEK) Tube |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ASTM D638 |
| Tensile Strength | 105 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 30 | % | ASTM D638 |
| Flexural Modulus (143°C) | 3400 | MPa | ASTM D790 |
| Flexural Strength | 137 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648 |
| Melting Temperature | 340 | °C | DSC |
| CLTE - Flow | 4.7E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Oxygen Index | 38 | % | ASTM D2863 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5140R B1 | Spartech Polycom | PP, Unspecified | Spartech |
| Moplen EP540P | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| FLEXOMER™ ETS-9078 NT 7 | The Dow Chemical Company | VLDPE | FLEXOMER™ |
| PAmpellonne® 607s | Politem Plastik Ltd. | Nylon 66 | PAmpellonne® |
| LNP™ THERMOCOMP™ MX88028 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |