Amodel® AT-1001L Datasheet,PPA,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Amodel® AT-1001L is an unreinforced, impact modified polyphthalamide (PPA) resin that exhibits exceptional impact strength at temperatures ranging from room temperature to as low as -40°F (-40°C), which suggests possible applications in ski boots and hockey skates. In addition, its chemical and wear resistance, combined with good mechanical properties, make Amodel® AT-1001L resin a prime candidate for applications such as anti-friction and wear resistant components, chemical, oil field, automotive and safety equipment. Natural: AT-1001 L NT

General Information
Additive	Impact modifier Lubricant demoulding
Features	Impact modification Low warpage Low temperature impact resistance Good chemical resistance Good wear resistance Hot water formability Lubrication ductility
Uses	Industrial components Industrial application Machine/mechanical parts Metal substitution Automotive Electronics Application in Automobile Field Oil/Gas Supplies General Shell
RoHS Compliance	Contact manufacturer
Appearance	Natural color
Forms	Particle
Processing Method	Water temperature mold injection molding Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1)

Physical	Nominal Value	Unit	Test Method
Density	1.11	g/cm³	ISO 1183/A
Molding Shrinkage			ASTM D955
Flow	1.7 - 2.2	%	ASTM D955
Transverse flow	1.9 - 2.1	%	ASTM D955
Water Absorption (24 hr)	0.75	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1900	MPa	ASTM D638
Tensile Strength (Break)	62.1	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	6.0	%	ASTM D638
Fracture	30	%	ASTM D638
Flexural Modulus	2210	MPa	ASTM D790
Flexural Strength	96.5	MPa	ASTM D790
Poisson's Ratio	0.35		ASTM E132

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
-40°C	750	J/m	ASTM D256
23°C	1100	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 3.18 mm)	120	°C	ASTM D648
Melting Temperature	310	°C

Additional Information
Penetration Impact, ASTM D3763, 73°F, Maximum Load: 1100 lbsPenetration Impact, ASTM D3763, 73°F, Total Energy Absorbed: 40 ft-lbsPenetration Impact, ASTM D3763, 73°F, Energy to Maximum Load: 30 ft-lbsPenetration Impact, ASTM D3763, -10°F, Total Energy Absorbed: 40 ft-lbsPenetration Impact, ASTM D3763, -10°F, Maximum Load: 1260 lbsPenetration Impact, ASTM D3763, -10°F, Energy to Maximum Load: 30 ft-lbs

Additional Information

Penetration Impact, ASTM D3763, 73°F, Maximum Load: 1100 lbsPenetration Impact, ASTM D3763, 73°F, Total Energy Absorbed: 40 ft-lbsPenetration Impact, ASTM D3763, 73°F, Energy to Maximum Load: 30 ft-lbsPenetration Impact, ASTM D3763, -10°F, Total Energy Absorbed: 40 ft-lbsPenetration Impact, ASTM D3763, -10°F, Maximum Load: 1260 lbsPenetration Impact, ASTM D3763, -10°F, Energy to Maximum Load: 30 ft-lbs

Injection	Nominal Value	Unit
Drying Temperature	110	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.045	%
Hopper Temperature	79.4	°C
Rear Temperature	304 - 318	°C
Front Temperature	316 - 329	°C
Processing (Melt) Temp	321 - 343	°C
Mold Temperature	65.6 - 110	°C

Injection instructions
Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	DhBFXs_Amodel-AT-1001L.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Rilsan® BESVOA FDA	Arkema	Nylon 11	Rilsan®
KEP® 210	Kumho Polychem Co., Ltd.	EPDM	KEP®
Hifax TYC 852P E C12716	LyondellBasell Industries	PP Copolymer	Hifax
Sylvin 83008-85 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
NEONIT® SK80 L8G	SBHPP	Epoxy	NEONIT®