MAJORIS FW195X - 1298
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DgpIP5_MAJORIS-FW195X---1298.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS FW195X - 1298 is a mineral filled high performance compound intended for injection moulding. MAJORIS FW195X - 1298 is intended for components, which require very good surface quality, rigidity, low shrinkage and high dimensional stability. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2850 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 30.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2160 | MPa | ISO 178 |
| Flexural Stress | 54.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 49 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 77.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 XP-636 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Quadraflex™ ALE-55D-B20 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Multilon® T-3750 | TEIJIN LIMITED | PC+ABS | Multilon® |
| Grivory® HTV-6H1 nat | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| Sylvin 8362-90 White 1557 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |