Hylex® P1303L2 HB
| Category: | PC , Polycarbonate |
| Manufacturer: | Entec Polymers |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dgid3D_HylexP1303L2HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYCARBONATE, UV STABILIZED, LOW MELT FLOW, MOLD RELEASE |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 61.0 | MPa | ASTM D638 |
| Fracture, 23°C | 57.9 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 6.0 | % | ASTM D638 |
| Fracture, 23°C | 96 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2330 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 96.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 810 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 131 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® 6261-P/D | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Unichem 1417-013 | Colorite Polymers | PVC, Flexible | Unichem |
| Nymax™ ND 1233 GF Black | PolyOne Corporation | Nylon 66 | Nymax™ |
| Nypol® PA B3 G15 NTLA010 NT317 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| OTECH TPO OTR8588 - Gasket | OTECH Corporation | TPE | OTECH TPO |