KumhoSunny PC/PET HTC6060
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PC/PET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dgho0c_KumhoSunny-PC-PET-HTC6060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HTC6060 is a PC/PET resin, offering high heat resistance, high impact and excellent chemical resistance. HTC6060 is recommended for automobile front grille, electrician products,etc |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 265°C/5.0 kg | 30 | g/10 min | ASTM D1238 |
| 260°C/5.0 kg | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.60 to 0.90 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 58.0 | MPa | ASTM D638 |
| -- | 56.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 2100 | MPa | ASTM D790 |
| -- 1 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 70.0 | MPa | ASTM D790 |
| -- 2 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 65 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
| Notched Izod Impact | |||
| 3.20 mm | 750 | J/m | ASTM D256 |
| 23°C | 65 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed) | 115 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 137 | °C | ASTM D1525 4 |
| -- | 130 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| 4 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 1206 LD | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Tecomid® NAX0 GR60 NL | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| Sindustris PP HM3208 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| TOTAL Polyethylene Lumicene® Supertough 32ST05 | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| Lucky Enpla LAY1001F | Lucky Enpla Co LTD | PC+ABS | Lucky Enpla |