LNP™ THERMOCOMP™ GF006 compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DgbpRp_LNPTHERMOCOMPGF006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP GF006 is a compound based on Polysulfone resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound GF-1006 Product reorder name: GF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.40 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.26 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 118 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8900 | MPa | ISO 178 |
| Flexural Stress | 165 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 2.2 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 184 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 182 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 5.9E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 - 338 | °C | |
| Middle Temperature | 338 - 349 | °C | |
| Front Temperature | 349 - 360 | °C | |
| Processing (Melt) Temp | 360 - 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 3190 | Teknor Apex Company | TPV | Sarlink® TPV |
| Vydyne® R515H BK02 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| NaturePlast PBI 003 | NaturePlast | Polyester, TP | NaturePlast |
| LUVOCOM® 50-0828 | Lehmann & Voss & Co. | PC | LUVOCOM® |
| Sylvin 83015-80FUV Brown 7463 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |