Order Products : sales@su-jiao.com
RTP 199 X 70836 A
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DgaBnq_RTP-199-X-70836-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.10 - 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8900 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 - 2.5 | % | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 179 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | 21 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2 | 28 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 155 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 3(2.00 mm) | < 100 | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 30.0 - 65.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 22/1, Compression ratio 2:1, Flight depth 5 mm minimum, in feed section, Screw diameter 16.5 20 mm minimum, Compression section length 12 - 13 diameters, Check ring valve assembly free flow type no restrictions, Nozzle orifice 6 mm diameter. Feed throat from hopper to machine must have sufficient opening to prevent bridging of long pellet composition. |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | Values per RTP Company testing. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 682 | RTP Company | ABS | RTP |
| SABIC® PP 513MNK40 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Durepol® PBT A3 G15 FR PRTA010 BT301 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| Gallonprene® GP410-9501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Sylvin 8887-95 Brown 7395 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |